AMD-3

AMD-3 LED resin produces dimensionally accurate and stable prints. Due to its stiffness and a fair amount of hardness it can sustain straight edges and print out even the tiniest features. Supports do not bend during printing, keeping the model in place throughout the whole printing session and giving a higher rate of success with complex prints. It exhibits low shrinkage so the print will not deform during post-curing stage and will not crack over a long period of time.

Resin is available in two colors: black and grey. Colour is almost fully opaque. Surface is glossy and hard (80-90 Shore D). After post-cure, print does not feel sticky or tacky. It does not scratch very easily. Due to its hardness, material’s surface can be polished to remove any layer lines, support marks or other imperfections. This allows using this material for printing masters for silicone casting and other applications where smooth surface is needed.

Water absorption is less than 0.2%. This means, that your models will not deform due to moisture or exposure to IPA. It is even resistant to some acids. Due to its resistant nature it is perfect for metal plating processes.

For a successful print, we recommend:

• Level your build plate.
• If it’s your first print with this resin, print something small first. We recommend this calibration model.
• Find initial printing settings here: AmeraLabs resin settings. 
• Use support column thickness of 1.5-2mm, support tip thickness of 0.2-0.6mm.
• Use attachment layer.
• Hollow your models.
• Use slower lift speeds. 5mm/min for bottom layers, 40-60mm/min for normal layers.
• Let us know if you have any trouble. We are here to help: Facebook messenger,  support@ameralabs.com

Viscosity of this material is relatively low – around 180-200cps – so cleaning is quite easy.
If you do not have ultrasonic cleaner of prefer cleaning with ordinary IPA baths, here is our 4 easy steps cleaning procedure:

1. After taking your printed object off the build plate leave it submerged in the IPA bath for 2 minutes.
2. Swirl the IPA bath with printed part in it actively for another 2 minutes.
3. After swirling, leave it still, but fully submerged for another 2 minutes.
4. Finally, swirl the bath actively again for 2 minutes.

Evaluate cleaning results and repeat this procedure only once (if needed) with clean IPA.

If you prefer cleaning with ultrasonic cleaner, we recommend to put a printed part into the container with IPA, close it well and put
the container into the ultrasonic cleaner filled with water. Leave it for no more than 10 minutes without additional heating.

If you use Wash and Cure station, leave the printed object submerged in IPA for 6 minutes. Depending on the results, you can repeat this step again and leave for additional 6 minutes.

It is easier to remove supports before post-curing. However, you can also post-cure a print with supports and remove them later. Depending on the model this can help to obtain better geometries if you have such goal. Post-curing time depends on your curing station. It can vary from 5 minutes to 1 hour (until the surface of your 3D print becomes non-sticky). You should post-cure immediately after cleaning and drying. After proper post-curing surface of AMD-3 printed objects should be completely non-sticky and very hard to scratch.

Tensile Strength at Break: 55MPa (ISO-527, post-cured) 
Elongation at Break: 6% (ISO-527, post-cured) 
Viscosity: 180-200 cPs (at 25°C) 
Hardness: 80-90 Shore D (ISO 868) 
Compatible UV Wavelength: 365 – 420 nm